Wednesday 17 February 2021

Recovering from Devitrification



An explanation of what devitrification is, can be found in the link.

Mild devitrification is generally a smeary appearance on the surface.  Most often this can be corrected by either removing the surface, adding a flux or putting another surface over the piece.

mild devitrification
photo credit: Bullseye Glass Co.

Removing the devitrified surface

Sandblasting and grinding are two common methods of removing the surface. If you have access to a sandblaster, this is the easiest method of removing the surface.  You can remove the surface with manual methods too.  You can use wet and dry sandpapers, starting with coarse ones and proceed through grades to at least 400grit (0.037mm).  The flexibility of the sandpapers is that they can conform to uneven surfaces that tack fusing provides, to remove devitrification in depressions as well as the high bits. Diamond hand pads and sheets do the job more quickly, but are more expensive.

Acid etching is another surface removal method. There are various etching creams on the market which will remove the surface. You need to apply and leave for a long time to allow the acid to work on the glass surface.  It is best to keep the acid paste damp to enable the acid to work over a long period.  A piece of cling film will work well.

Making a new surface

You can provide a new surface by using devitrification sprays.  There are both commercial products and do it yourself ones that work.  The do it yourself product is a borax solution.  The method for making the solution is given here.

Borax powder

You also can give the devitrified surface a new one by covering it with clear powders.  Powders sifted evenly over the surface until there is a thin covering over all the piece will give a new surface concealing or covering the devitrification.  Fine frit does not work so well, as more needs to be sifted over the surface.  This will not be applicable to tack fused pieces, as the whole piece needs to be taken to a contour or full fuse to make sure the powder or frit is completely smooth.  This will make the tack fused areas flat.

Left to right - devitrified surface, powder covering, fired piece
Photo credit: Bullseye Glass Co.

When dealing with devitrification, the whole of the surface should be treated, not just isolated areas.  Treating isolated areas will most probably leave a difference in appearance between the treated and untreated areas.  It is not worth the risk of having to fire yet again.


Dealing with devitrification usually involves removing the devitrified surface or making a new one.

Wednesday 8 November 2017

Kiln Wash Removal


There are a variety of ways to remove kiln wash.  Many depend on whether the surface is flat, smooth curves, angles or textured.  Some are applicable to both.

Flat surfaces are the easiest to deal with.

Abrasive methods work well with a variety of tools. 

They can range from large paint scrapers to smaller ones with a Stanley blade inserted. 






Coarse open mesh plaster board (dry wall) sanding sheets are very useful. There are frames that you can fix them to, but sanding without the frame works well too.





Using power tools to sand the shelf is not advisable.  It is too easy to remove lots of material, including the surface of the shelf – even the hard, ceramic ones.  This leads to minor depressions in the shelf and consequent bubble difficulties when firing.

Do not be tempted to sandblast as that will, almost certainly, create small depressions in the surface of the shelf.  Sand blasting is only possible on steel moulds.

Wet

Wet methods are applicable if you are concerned about the dustiness of the process.  You can dampen the kiln wash on the shelf and sand or scrape as above.  You will create a paste or slurry in front of the scraper which can be bagged and put in the waste.

You can also use a lot of water and the green scrubby washing up pads.  Unless you use a lot of water, the kiln wash builds up in the scrubbing pads.





Some people use vinegar or chemicals such as lime away with the water. Both are acids – lime away being much the strongest.  I am sure these are used on the basis that kiln wash is based on lime.  However, the material that makes the kiln wash stick to the shelf is china clay which is barely affected by the chemicals.  In addition, the alumina hydrate is impervious to many chemicals available to kiln workers.

One drawback to using wet methods, is that the shelf is wetted and needs drying before use.  The amount of water used in applying kiln wash is minor in relation to washing or soaking the shelf to remove the kiln wash.

Do not be tempted to use pressure washers. Yes, they will remove the kiln wash, but also leave little divots in the shelf which will cause later problems.

Smooth curves
Kiln wash on moulds with smooth curves can be removed with flexible sand papers or the plaster board sanding screens.  Normally, the coating of kiln wash is thin and does not require a lot of pressure or effort.

It is possible to dampen the kiln wash and take it off with scrubbing pads.  Make sure you do not use excessive pressure.  If you have wetted your ceramic mould, you need to dry it very carefully, to avoid having the mould break in the next firing.  This is because trapped water can turn to steam and the pressure will break the ceramic. It is best to let the mould air dry for a week or so before putting it into the kiln to thoroughly dry at about 90°C for a couple of hours.

Do not be tempted to use a pressure washer or water pick, as both can erode the surface of a ceramic mould.

Curves with angles

Moulds with angled areas such as at the bottom or corners of a rectangular mould need a flexible abrasive to clean out the angles.  You can fold a piece of sand paper to use the folded edge to do the final cleaning out of the angles.

The same can be done wet, but all the precautions about wet removal of kiln wash need to be observed.

Textured
Textured moulds require much more care in cleaning the kiln wash away, to avoid damaging the images and textures.  The flat upper surfaces can be dealt with as though it was a flat kiln shelf.  The indentations need to be more carefully treated.  Folded pieces of sand paper can be used to clean the delicate areas.

To ease cleaning of textured moulds it seems best to use kiln washes without china clay as the binder.  These will brush out of the mould with a fibreglass bristled brush.  It is now popular to use boron nitride - often sold as Zyp - as a coating for these moulds.  This needs to be brushed out and renewed with each firing.


Removing kiln wash from glass

Kiln wash stuck to the glass can present greater problems, because you want to avoid marking the glass.  It is best to start with the least aggressive abrasive, such as a green scrubby, and progress toward more aggressive and abrasive methods.  When using the more aggressive methods, try the finest grit first to see if that will work, as it makes for less work cleaning up the grinding marks from the glass.

For flat glass, you can work with a succession of finer loose grits, or a succession of finer diamond hand pads.  




Flexible diamond impregnated sheets can be used for curved surfaces.  Again, this requires a succession of finer grits to get to the polished stage.





You can use small hand held rotary tools with diamond and felt pads to polish out stuck kiln wash.  This helps to remove some of the labour of polishing the glass.





Some people advocate the use of acids to remove the kiln wash.  However, you must remember that glass is an alkaline material and acids will tend to mark the glass.  Vinegar is a mild acid, but prolonged exposure will etch the glass.  Strong chemicals such as lime away or etching cream or hydrofluoric are all strong acids and will mark the glass after brief exposure to them.

Tuesday 15 May 2012

Glass Stains

A lot of people want to use old window glass – for recycling reasons, for the character of the older glass or because it is cheap or free. This glass often has stains or the appearance of corrosion or etching from age or storage conditions. To remove these blemishes you should start from the least aggressive method and work your way through the more aggressive methods until you find one that achieves the cleanliness you desire.


When using these methods appropriate breathing and hand protection are a requirement. 

Surface deposits
The first method is to wash the glass in water with a bit of crème cleaner. Place the glass flat on a work bench and scrub it with a brush containing the water and cleaner. Rinse and dry. This may be all that is needed.

More persistent stains require chemicals. Use rubber gloves for this kind of process. Soak the glass in a dilute (5-10%) solution of lye. This is also known as caustic soda. Chemically it is sodium hydroxide (NaOH). After the soak wipe with a disposable towel and dip it into a dilute solution of hydrochloric acid (5-10% again) or vinegar to neutralise the caustic soda. Wipe the glass with a towel and rinse with plain water and polish dry.

Metallic stains or iridescence and etched surfaces
If the blemishes are more than surface deposits, more aggressive methods are required. The metallic-like stains and iridescence are usually evidence of the corrosion of the surface of the glass. These and any etching require grinding and polishing.

You should start with a polishing process to determine if that will be sufficient to bring clarity back to the glass. The use of an optical polishing material such as cerium oxide paste and a felt polishing head is often enough. Ensure that you do not let the cerium oxide get any drier than a paste to avoid localised heating and therefore breakage of the glass. Rinse the glass in clean water and polish dry.

If this does not remove enough of the surface to provide the desired clarity of the glass you can try either using pumice or jeweller's rouge, or dilute hydrofluoric acid.

Hydrofluoric acid used in a 10% or less solution will remove the surface of the glass, so eliminating the evidence of corrosion. It will even out, but not eliminate, the evidence of any etching. The disadvantage to this method is the risks associated with such a dangerous chemical. There is within this note on acid etching a door panel some advice on safety.

If you decide to avoid the hydrofluoric acid method, you can use mild abrasives such as jeweller's rouge or pumice with water and a felt polishing head. Once you have ground the whole of the surface, you need to wash it very thoroughly in clean water. Then change the felt head and go to cerium oxide to provide the optical finish.

Note:
All the dilutions and solutions suggested here are with water.

This note assumes the glass has had any paint already removed. For a method of removing house paint see this tip.