Bas Relief Moulds

Bas relief moulds that have an image carved into the surface are popular at the moment. They are most often called texture moulds.  The image is “carved” into the back of the glass, creating uneven thicknesses of glass that refract the light to show the image through the smooth plane of the front.

One of the problems with these kinds of moulds is that lots of bubbles are created, often very large ones.  This results from the many places where the air cannot escape from under the glass during the forming process.

Solutions

There are some strategies that can help avoid these bubbles.

Use the 6mm rule

Fuse the glass into a six-millimetre thickness first.  Two layers of glass give more weight to help the glass conform to the texture of the mould.  It also resists bubble formation more than a single layer.

Use the Low and Slow approach

It more important to have low and long bubble squeezes.  The most successful strategy will have a slow rise in temperature to put as much heat work into the glass as you can before the bubble squeeze.  The bubble squeeze is the most important part of firing these texture moulds.  It will start at about 600°C rising at only about 25°C/hr to around 680°C – that is, taking three to four hours. 

Use slow rates of advance

A third element is to rise slowly toward the forming temperature.  Possibly nothing faster than 75°C.  This enables you to keep the forming temperature much lower than a fast rise will.  The usual temperature recommended is about 780°C.

By using a slow rate of advance you can probably reduce the forming temperature by about 20°C.  You will need to peek at intervals to be sure the glass has taken up the required texture. Again, it is about putting as much heat into the glass at as low a temperature as possible.

Use Long soaks

An alternative to the slow rate of advance is to use a long soak at as low temperature as seems suitable.  You will need to peek at intervals to determine when the texture is achieved.  When the appropriate texture is imparted to the glass, you need to advance to the next segment.  This means that you need to know how to get your controller to skip the following segment.  Or, if the texture is not achieved before the end of the scheduled soak, how to extend the soak time.  If you are using 760°C as you target temperature with a rise of 150°C, you may wish to soak for about an hour or more.  Remember that this is in the devitrification range.

Alternative - Frit

A completely different approach is to use fine frit and powder to give a patè de verre appearance by sintering the frit.  This eliminates the bubble problem entirely.

You will need a lot of frit if you are trying to make a sheet of 6mm from the frit.  You could just take the sheets of glass cut to the size of the mould and smash them up to get the required amount of glass.  Or you can use your cullet, by weighing and smashing up enough glass. 

The calculations for weight are best done in the metric system (in cm) as there are easy conversions between volume and weight.  Assume your mould is 20cm square.  The area is 400cm².  The volume is that times 0.6cm or 240cm³.  The specific gravity of glass is approximately 2.5, so you multiply the volume by that and get 600gms of glass required to get a 6mm thick sheet. 

You could full fuse this into a clear sheet, although this would take a much higher temperature and longer soak that would be good for the mould. Better is to sinter the glass.

To sinter the glass, you need slow rises in temperature and long soaks.  A rise of about 75°C to the softening point of the glass (around 600°C) followed by a very slow rise (ca. 25°C per hour) to about 660°C is needed to allow the small grains of glass to settle together.   At the upper end of the bubble squeeze you need a three- to four-hour soak to sinter the glass. The thicker the layer of glass frit, the longer soak needed to ensure all the particles are heated.  The densest glass will be formed by a 50/50 combination of powder and fine frit.

Much better is to have a much thinner sheet formed from the frit.  This will be about two to three millimetres thick.  The weight of powder and or frit can be determined by the formula above, substituting 0.2 or 0.3 for the thickness.  This frit mixture needs to be evenly spread over the mould, with as much on the high points of the mould as the low ones.

If the mould has a lot of variation in height, you can sinter the frit mixture as a flat sheet first.  Then place it over the texture mould and give it a slow rate of advance to the to the top end of the bubble squeeze and soak for an hour or more, as required.  This will ensure you get the same thickness across the whole piece even though there differences in height.

The resulting piece will be very light and translucent.  It will have a fine granular feel to the touch.  It will have the same shape on both sides of the piece, with the upper surface having a slightly more shiny appearance than the bottom.

Further information is available in the ebook Low Temperature Kiln Forming.