Tack fusing multiple layers

The question:

Full fused 6mm base, with 3mm tacked pieces. It is to be tack fused and slumped now.  Does the number of fuse firings affect the rate of advance, and how long a soak will be required to slump it? 

Multiple firings

If properly annealed each time the glass is fired, the number of firings does not affect how the glass should be fired.  This assumes the same number of layers are being fired.

Tack fusing

Tack fusing this piece will need some care.  The portion to be tack fused is 3 layers thick – overlapping white pieces surmounted by the yellow balls.  The base layer is shaded from the heat by the white, which is generally slower to transmit the heat than many other colours. Bullseye suggests doubling the total height and firing for that thickness. Bob Leatherbarrow suggests 1.5 times the total height for creating the schedule.  Firing Schedules for Kilnformed Glass,  p. 124-6

In this case, because of the amount of white, I would go with the Bullseye suggestion.  My researches for "Low Temperature Kilnforming" also indicated that a tack fuse requires a schedule for two times the thickness. Other levels of tack fusing require different calculations.  The total height of 15mm will be treated as 30mm for scheduling purposes.  This is midway between the thicknesses in the published table.  The rates and times in the table are linear. You can calculate a mid-point in the schedule to get the numbers for your piece.  Half the difference between 25 and 38 is 6.5mm giving 31.5mm.  Using the half-way point will be slightly more conservative than using exact calculations.  It is so close as to make no significant difference.

You will notice that the table gives only annealing times and rates.  There is way you can use this table for the getting initial heating rates.  Look at the final cooling rate for the thickness. If the glass can survive the cooling rate given without showing stress, it will also survive that rate of increase.  The mid-point between 90 and 45 is 67.5°C.  This gives an initial rate of advance (68°C) which can be applied for this piece that has so much shading of the base layer. It should allow the heat to transfer through the white to the base layer without great temperature differences between the covered and the uncovered base layer.

As there is a lot of work in this piece, and it is for someone else, you can be cautious.  Introduce a soak at 260°C of about 30 minutes.  This will help to ensure the heat is distributed to the bottom layer.  If you want to be even more cautious, you can introduce a second 30-minute soak at 371°C before continuing to 540°C.

At 540°C you have passed out of the brittle zone of glass and can increase the rate of advance to 167°C per hour.  The amount of heat work you have put into this piece by the slow rate of advance may enable you to complete the tack fusing with a soak at 720°C.  You will need to observe when the appropriate amount of rounding has been achieved. You will then be able to advance to the annealing portion of the firing. 

For this piece, the annealing soak will be for 5 hours with a cool of 11°C per hour for the first 55°C. Then 20°C per hour for the next 55°C and a final cool of  65°C per hour. This anneal and cool will be about 21 hours, in addition to the ca. 21 hours, in addition to about 10 hours heat up, so don’t expect a quick firing.  Plan two days for the tack fuse.

Slumping

Slumping will need care too.  The piece has uneven layers and the same care is required as for tack fusing.  Experimentation has shown me that scheduling for an additional 3mm (1/8") is needed to ensure the piece is thoroughly heated throughout its thickness.  In addition, the white is stiffer than the other colours and will not bend so easily.  This kind of slow schedule means the glass will be at the same temperature throughout as the slumping starts.

Because of the slow rates of advance, you may be able to slump this piece at 620°C with a significant soak time.  You will need to observe when the piece is fully slumped.  Be prepared to advance to the annealing and cool segments of the schedule.  Some times you need to extend the hold time.  Be prepared for this too. The annealing time and cooling rates will be the same as for the tack fusing.

Further information is available in the ebook Low Temperature Kiln Forming.