Slumping and Draping materials - Kiln Forming Myths 12

Always slump into ceramic, drape over steel

This myth is based on the fact that steel expands and contracts more than glass and ceramic expands and contracts less.

So, the myth goes, slumping into steel means the glass will be trapped or crushed by the contracting steel.  But draping over means the steel will contract more than the glass making the removal of the glass easy.

The reverse is the expectation for ceramic.  Slumping into the ceramic allows the greater contraction of the glass to be removed from the mould without sticking.  But draping over means the glass traps itself against the ceramic as a result of its greater contraction.

These things are true.  But….

The most important thing in considering a mould is the draft.  This not about cold air, but the angles of the mould. A mould with vertical sides will not release the casting or kiln formed object even if the expansion characteristics of the two materials are identical. To release, the mould must have a slight angle from the vertical away from the glass.  This applies whether a slump or a drape.  This is called a positive draft, as illustrated.

www afsinc org

 And here

If the draft is sufficient, it does not matter whether you are slumping or draping into steel.  In using a stainless steel mixing bowl for draping, you can only use the lower portion where the angle is shallow.  If you rest the glass on the rim, the draft will be too steep to allow the glass to slide upwards as the steel contracts on cooling.

www evetsourcesolutions com

Even when draping over steel, you need to have a draft to aid the easy removal of the glass, as in this example:

creativeglassguild co uk

When draping over ceramic, you need to be careful that you have sufficient draft over the whole of the mould. In the case of this ceramic draping mould you need to make sure the glass is not fully formed as the steep portion at the top will be where the glass grabs the mould.

glassartbymargo com

And if you were to use this casting mould as a slumping mould, the steep straight sides would make it difficult to get the glass out of the mould. 

sundanceglass.com

Although the facts behind the statement “slump into ceramic, drape over steel” are established, you need to understand that the draft of the mould is as important as the way in which you use the material.

All myths have an element of truth in them otherwise they would not persist.

They also persist because people listen to the “rules” rather than thinking about the principles and applying them.  It is when you understand the principles that you can successfully break the “rules”.

The 6mm Rule - Kiln Forming Myths 11

Glass always wants to be 6mm thick

This is true only at some temperatures.  

The surface tension or viscosity of the glass, together with gravity determines the extent to which the glass will thicken or thin.  The viscosity of glass is such that at high temperature tack and full fusing heats, the glass does tend to become 6mm - 7mm thick. This is taken advantage of in kiln forming to obtain rounded edges, and in making frit balls.  A single layer of frit up to about 10mm will become a round dome due the action of the viscosity and weakness of gravitational forces acting on a small mass. 

Larger pieces of single layer glass begin to shrink as the viscosity is great enough to overcome gravitational forces to allow thickening at the edges.  This causes dog-boning.   At the same time the glass is thickening at the edges, it is thinning in the interior allowing large bubble formation on thin pieces. It also is the cause of the needle points on thinner pieces at higher temperatures.  The glass is soft enough to conform to any imperfections in the surface and so be stretched thin as the main mass of the glass contracts. 

This contraction also applies to low mass items such as frit in casting moulds.  The glass particles contract to form a single mass of material, leaving some stuck to the mould. These pieces may be completely separate as tiny frit balls, or if attached to the main mass, a series of needle points on the edge of the finished piece.

However, the viscosity at full fuse temperatures is not great enough to keep thicker glass in its original shape.  So the effect of gravity on glass of 9mm or thicker overcomes the weakening viscosity force and the stack begins to expand. The extent of the expansion is the result of both viscosity (heat dependent) and gravity (mass dependent).

At lower temperatures, the viscosity is much greater.  This can be used for low temperature tack or laminating temperatures. The glass can be adhered with heat without distortion of the single layer, as the viscosity is so high the glass does not change shape, even retaining sharp edges, although stuck together.

At temperatures above full fuse the viscosity decreases further allowing the glass to flow.  This is used in casting, blowing, and various higher temperature processes, such as aperture melts and stringer formation.  Here the viscosity is low enough to allow gravity to make thin and elongated shapes.

There is a range of temperature above which glass will thin more than the 6mm – 7mm “rule”.  I do not know the exact correlation between temperature and thickness, but at around 1150°C  the glass will become only a little under one mm thick.  This can be seen from the results of kiln runaways. The glass that is melted onto the surface of the shelf is extremely thin, showing that the viscosity was so low that gravity was able to thin it to a fraction of what we think of as normal thicknesses.

The 6mm myth arises from the behaviour of glass at a specific heat range and is the result of the combined forces of viscosity and gravity.  Knowledge of how these interact can enable you to understand the outcome of various projects.  This knowledge of the forces can be used to help create the effect you want.  It also enables you to employ various means to counteract the natural forces of gravity and viscosity. 

More information is in the e-book: Low Temperature Kilnforming.

Absolute Firing Temperatures - Kiln Forming Myths 9

There is a given temperature for each level of fusing – slump, tack, full, etc.

You will often see statements about the temperature for achieving a particular effect.  It is as if all glass under all circumstances does the same thing at a given temperature. These temperatures can only be understood in relation to several things.

• ·         Kiln characteristics
• ·         Speed of firing – i.e., heat work
• ·         Time at forming temperature

The relevant factors about the kiln are:

·         Insulation.  The two main types of insulation in kilns are fibre blanket and insulating brick.  Fibre blanket is often the main insulating element in kilns as it does not absorb a lot of heat. It of course loses heat more quickly than refractory brick.  Most often the floors of kilns are made of brick for rigidity and resistance to damage.  (They also can be replaced individually if one is damaged.)  Refractory brick comes in two densities.  The light weight one is not rated to such a high temperature and loses heat more quickly than the higher temperature rated dense brick.  Both lose heat much more slowly than fibre blanket.  This means the top temperature can be reached more quickly in a fibre insulted kiln than in brick insulated kilns. The brick insulated kilns radiate the heat back into the kiln upon cooling, making for long safe anneal cools without much effort in controlling the cooling rate. Thus the temperatures for an effect are different for kilns with bricks all around than with fibre blanket, and no comparison is easy between kilns with different insulations.

·         Size.  The size of the kiln has an effect on the temperature cited to achieve an effect.  A small kiln can heat up very rapidly, but the glass cannot heat evenly as quickly.  A large kiln takes more time to heat up, as there is more insulation absorbing the heat input.  So working temperatures for small and large kilns are different.  The size of the piece(s) of glass also have an effect.  Small pieces can be heated much more quickly than large or thick pieces, so the top temperature for an effect will be different for the two sizes.

·         Temperature variation across the kiln shelf affects the rate of firing possible and (as noted later) will affect the top temperature.  The more even the heat the faster it is possible to go and that affects the temperature chosen.

·         Element placement.  Some kilns have only side elements, some only top elements, and some have both.  All these variations affect the temperature required to obtain an effect.  In general, top fired kilns can be fired faster than side fired kilns.  Kilns with both, require an intermediate rate, unless the side and top elements can be fired independently.

Speed of firing, i.e., heat work

·         Heat work factors make the top temperature different in different circumstances.  This is mainly about the speed at which you fire the glass.  Generally, the slower you fire, the lower temperature you need.  Allowing the glass to absorb the heat gradually usually means that you can achieve a particular effect at a lower temperature.  A fast rise in temperature requires a higher temperature.

Soak times 

·         The amount of time you soak at the working temperature will also affect the temperature chosen.  A longer soak allows a lower temperature to be used (although that can get into the risk of devitrification from spending too long at the top temperature – it is a balancing act).  A higher temperature can be used to keep the soak time reduced. 

All these variables mean that without being given the kiln characteristics and a schedule, you cannot evaluate the temperatures and rates of firing that are given out by others.  You need to know how closely their kiln fits with your kiln in its characteristics as outlined above.  When asking for a temperature or a schedule, you should indicate what kind of kiln you are using.  You need to know in any schedule what the ramp speeds are and the soak times.  They can then, of course, form the basis for your experimentation.

All myths have an element of truth in them otherwise they would not persist.

They also persist because people listen to the “rules” rather than thinking about the principles and applying them.  It is when you understand the principles that you can successfully break the “rules”.