Soldering Radiating Lines

Some times no matter how you try to avoid it in the design, you end up with multiple solder lines joining at one point.

In copper foil work, I find it best to tin all the copper foil before assembly, as this means you can use a minimum of solder to tack solder the pieces to one another.

You will be left with less solder at the joint if you start from the joint and move away from it while soldering. This drags the solder into the bead line rather than letting the solder build up at the joint of the multiple lines and give a resulting high point resulting from the accumulation of solder there.

Kiln Furniture

You do not have to buy all your kiln furniture. Any refractory material – any heat resistant material that will stand up to the forming temperatures – that you have from broken shelves or used material will do.

The advantage to home made kiln furniture is that you can have exactly the shape you want. There are a number of possibilities.

Example of broken shelves

 Broken kiln shelves can provide supports and dams. They can be cut with a tile saw to give long strips that can be used as dams. Smaller squares and rectangles can be stacked to give height to other supports for the glass.

Cutting a shelf with a hand saw

25mm vermiculite board

Vermiculite in the form of a pressed board provides a medium strength kiln furniture. It can be cut with a wood saw, although it dulls cutting tools quickly. The board can also be carved with wood working tools although it is very abrasive, requiring tools to be sharpened before use on wood again.

25mm ceramic fibre board

Fibre board is not as strong or rigid as kiln shelves and vermiculite are, but is much more adaptable to curves and undulations. They can be cut with a knife and used with or without hardener – colloidal silica. If the hardener is used some kind of separator will be required to keep the glass from sticking. Dust masks are required for working with ceramic fibres.

Soft fire brick

Soft fire brick can be cut with a hand saw into many shapes and and sizes. They are suitable as supports and braces for dams.  There are also higher density bricks that are much heavier to resist the movement of dams.

3mm fibre paper

Fibre paper can be cut and stacked to provide shims to level shelves and moulds. Shapes can be cut into stacked layers of the material to provide dams for irregular shaped projects.

Uneven Slumps

Uneven slumps are an occasional feature of kiln forming. There are a number of possibilities that can cause this.

A mould that is not level will lead to an asymmetrical slump. You need to make sure on each firing that the mould is level, as well as your kiln and the shelf or supports. A three-way level can check this quickly.

Glass that is placed unevenly on the mould can cause uneven slumps. The glass should be placed on the mould so that it is equidistant from the edges of the mould all the way around. The glass needs to be level too. Again the three way level can help.

A slight bevel on the bottom edge can help avoid any catching of the glass as it moves within the mould.

Baffling or shielding parts of the glass can keep the heat off areas that tend to heat up faster than the rest and so begin moving before other parts of the blank.

Deep moulds most often present difficulties with uneven slumping. The best approach here is to use multiple, progressively deep slumps.

It also is possible to reach in with a wet stick and move the glass back to an even slump during the firing. Please observe all the safety requirements.

Most importantly, slow temperature rises solve most of the problems of uneven slumps. Fast temperature rises allow the component parts of the piece to absorb heat differently for different colours and glass of different viscosities. Slow rises in temperature help avoid any unevenness in the way the kiln heats the piece. Slow rises give more control and achieve the result at a lower temperature.

Note that a number of the solutions require observation while firing. The best results come from observing what is happening in the kiln. It allows you to make corrections either while firing, or – more often – in the next firing of a similar project.

Leaking Cutters

People sometimes comment that their cutters are leaking. Most cutters of the pencil type are not prone to leaking. Some of the pistol shaped cutters seem to have more difficulty.

One possibility is that the oil being used is too thin for the system that dispenses the oil. In that case a little thicker oil may cure the problem.

It may be that the oil is leaking from some where else than the valve or wick that is intended to dispense the oil. This sometimes happens when excessive pressure has been put on plastic handled cutters whether pencil or pistol. In this case, the alternative is to replace the cutter or use another method.

The other method could be called the dip and cut method. In this case you leave the reservoir empty and have a shallow container filled with oil soaked cotton wool. Dip the cutter wheel into the cotton wool before each cut and this will give you enough lubrication for the score. A variation on this is to dip a brush in a container of oil or turpentine substitute and paint along the line of the cut before scoring. Both are effective.

Although it is not a repair, you can push a cotton wool lump down to the valve or wick, saturate it with oil and then there is enough oil to lubricate the cutter wheel, without an excess to leak out. You do need to renew the oil for the lump of cotton wool from time to time.

Reworking Designs

Principles of design practice for stained glass, 5

Having created the design, you should consider re-working the designs for a variety of reasons. Some of these are:

- to save time in the later stages of the work. It all too easy in the excitement of creating a new piece to want to get directly on with making, however this often gives construction or design difficulties that have to be solved in the making, leading to compromises. In general far too little time is spent in the design stage. Time spent on the design will be more than saved in the construction and will produce a more satisfactory piece.

- to ensure the structural stability of the piece. Although reinforcement should be considered from the beginning of the design, this is the time to ensure that the piece will stand up to the use it will receive during its – expected – long life.

- Make sure you have investigated every possibility to answer the challenges of your design.

There are a number of activities that can help with these elements.

Reworking will enable you to maintain the essence of the design while simplifying lines and easing the labour of the construction of the panel. Often the design contains a number of lines that are not essential to the whole design.

As you re-work the design, you can make sure every curve, dip and angle are to your liking and so improve the whole. Redrawing also helps understanding of the design and the placing of lines. It will also help in considering the placement of lead came and the widths to be used.

Make sure the design is still structurally sound. The design should avoid long nearly straight lines with few interruptions, especially those that go from edge to edge in any direction. The lines should interlock rather than have many joins onto long lines.

It gives an opportunity to ensure that you can cut all the pieces. This is the time to look at the negative or background pieces to make sure you can cut them as well as the foreground pieces. Usually people are so concentrated on designing the main image that the background becomes too complicated to cut easily.

Make successive tracings with each change, so there is a record, allowing you to step back wards to an earlier version if necessary.

If this re-working stage leads to the realisation of design problems, there are some things that can be tried:

• Cropping the design can transform it. The focus of the design can be enhanced by removing some of the surrounding “information”. The change of proportions say from landscape to portrait can make significant differences.
• Enlarging and using only a portion of the original design can be a solution. This is similar to the cropping operation, but has the added advantage of making the pieces larger and easier to cut.
• Further simplification of background design lines can be considered. This will bring the focus back onto the main part of the image.
• Changing relative proportions can transform the design, e.g., by enlarging a busy background, it can be made simpler and easier to read the whole panel.

Elements of Design:

Designing for strength 

Colour selection

Design lines 

Design sources 

Reworking designs