Care of Ceramic Kiln Shelves

Mullite kiln shelves
credit: IPS Ceramics

The most popular and easily available ceramic shelves are made from Mullite, Cordierite, and CoreLite. Other hard specialist kiln shelves are available. They are made of other materials. Shelves are also made from other materials such as refractory fibre board, vermiculite, and fire-resistant ceiling tiles. This concentrates on the care of ceramic shelves.

Composition and Characteristics

This table gives some information about the characteristics of the materials involved in these shelves.

 

Name	Thermal Shock Resistance	Brittle	Strength	Composition
CoreLite	Low	Yes	Moderate	Ceramic with a high silica content
Cordierite	High	Yes	Strong, but heavy	Magnesium, iron, aluminium oxide, silica
Mullite	High	Yes	Strong. but heavy	Silica, Aluminium oxide

 

CoreLite is a trade name for an extruded ceramic shelf. It is strong, but brittle. It is subject to thermal shock below 540ºC/1000ºF. This suggests the ceramic has a high silica content as the quartz inversion is at 573°C/1063°F, where the ceramic has a sudden expansion on heating and an equal contraction on cooling. The cooling rate at this temperature is normally slow enough to avoid breakage.

credit: Clay Planet

cordierite - composed of magnesium, iron, aluminium oxide, and silica. hard, brittle, and with low expansion characteristics.

credit: refractorykilnfurniture.com

Mullite –composed largely of silica and aluminium oxide. It is strong, brittle, and has good thermal shock resistance.

Care

There is enough information from considering the composition of these shelves to indicate they are all brittle and have differing vulnerabilities. These have implications for storage, use and cleaning.

Storage

If storing vertically, take care to avoid setting down on hard surfaces. If they are in a rack, have a separate slot for each shelf. This avoids friction between shelves and possible surface scratches. The most useful material for these racks is wood, or harder materials covered with wood. These racks can be horizontal or vertical.

If it is not possible to have a separate rack for each shelf, do not lean them on each other. Shelves leaning against others or against hard surfaces can become scratched. Provide a cushion against scratches such as cardboard, or thin plywood.

When moving the shelves, avoid setting them down on their corners, or bumping the shelf anywhere against hard structures.

Use

Reduce firing speeds to less than 220ºC/430ºF per hour up to 540ºC/1005ºF, especially for CoreLite shelves. Cordierite and Mullite shelves are not as sensitive, but still can be broken by fast firing rates in this temperature region.

Cover a large portion of the shelf at each firing to avoid uneven heating of the shelf. It is best to evenly distribute moulds and other things that shade the heat from the shelf around the shelf to help avoid thermal shock breaks.

If you cannot or do not want to cover the whole shelf, elevate the mould(s). This helps to keep the whole shelf at the same temperature when only small parts of shelf are covered. It does not seem to matter so much when flat glass is in contact with the shelf. But continue to observe the moderate ramp rates below 540ºC/1005ºF.

It is even more important to elevate damp or heavy moulds from the shelf. These kinds of moulds shade the heat from the shelf immediately below them while the rest of the shelf heats rapidly. This difference in expansion over parts of the shelf becomes too great for the shelf to resist.

Another thing to avoid is cutting fibre or shelf paper on top of the shelf. It often creates long shallow scratches in the shelf. These can be the source of bubbles, but more often, flaws on the back of the fired pieces.

Cleaning

Care is needed to avoid mechanical damage during cleaning. Scraping can create scratches in the shelf. These are difficult to remove or fill smoothly. So, scraping needs to be done carefully.

Any sanding also needs to be done carefully. If you use power tools, it is very easy to create shallow depressions that will be the source of bubbles in future firings. It is slightly more time consuming to manually sand the kiln wash with a sanding screen with or without a holder. But it preserves the flatness of the surface.

If it is decided to wash the shelf primer off the shelf, consider how difficult it is to wash a very persistent baked on substance. It requires thorough scrubbing to remove all the hardened material. Power washers are not advised since the high water pressure can abrade the surface of the shelf.  But if you do decide on washing, you need to air dry for several days afterwards. Then kiln dry slowly to just below boiling point of water. Soak at that point for several hours, or until a mirror held above the open port does not fog up.

There is more information on removing kiln wash here and here.

Summary

Ceramic kiln shelves are hard, but subject to scratches, impact breaks, excess dampness, failure due to uneven temperatures, and to rapid rises in temperature below 540ºC/1005ºF.