Making Thin Sheets

The question of how to make thin sheets arises from time to time.  Unless you are a glass manufacturer, it is unlikely you can make large, thin glass sheets.  But you can approximate making thin sheets by two methods that I know.

Sintering

One of these is sintering.  This is firing the glass to a low temperature and soaking for a long time.  The common form of this is powder wafers. 

By using a screen to deposit an even layer of glass powder you can make very thin, but delicate sheets of glass.  The procedure I would use is a screen of about 45 – 60 threads per inch.  This is coarse enough to allow the powder through, but not so fine as to “reject” large amounts of the coarser particles. 

You can screen the powder directly onto a kiln washed shelf, or onto Thinfire or Papyros.  You will not be able to move the unfired powder on a sheet of paper or fibre paper without changing the thickness and shape of the screened powder.  It must be laid down onto the separator directly on the shelf.  You can of course, move the shelf to the kiln if you can get in without tipping it.

Method

Support the screen about 3mm above the surface to allow the powder to fall through.

Make a ridge of powder at one end of the screen.  Using a smooth straight edge wide enough to cover the whole of the screen, lightly spread the powder from the starting end to the other. Then repeat drawing the powder to the starting end.  Make about five repeats of this – that is 10 passes, to get enough powder laid down to form about 0.5 to 1mm sheet.  You will need to experiment with the number of passes to get what you want.

Do not try to press the powder through the screen.  That will only wear the screen out quickly and may tear it.  Each pass should be a light spreading of the powder.  It is heavy enough to fall through the screen without additional force.

You could, of course, just sift the powder over the area you want to cover and judge by eye how even the layer is.  It is possible that your observation is good enough, but it is more likely that you will have thick and thin areas.  Often even at sintering temperatures, the thin is pulled toward the thicker, leaving small or large holes.   By screening the powder, you know you will have an even layer

Firing

The kind of schedule to use to sinter the glass particles together without changing their structure is the following:

220°C to 482°C , soak for 60 mins
55°C to 593°C, 10 minutes
28°C to 665°C for 5 mins
as fast as possible to 482°C for 30 mins
28°C to 427°C, no soak
55°C to 370°C, no soak
110°C to 50°C, no soak

This will work for most fusing glasses.

This slow firing allows enough heat to penetrate the glass grains that they will stick together without changing shape or developing holes.  I admit the anneal cool is very cautious.  You can experiment with quicker cools if you want to speed the process.

  

Pressing

This is a technique of thinning already existing sheets of glass.  Typically, you will have a 6mm or thicker piece of glass that you want to be 3mm or less.  Paul Tarlow has described this kiln pressed glass very well in his books and on the fusedglass.org site.

In essence, you use a pair of kiln shelves.  Kiln wash both shelves.  Place the glass to be thinned on one shelf.  At the outer edges of the shelf put down spacers of the thickness you want the glass to be after pressing.  This will keep the upper shelf from settling down too much and more importantly unevenly.  Place the other shelf, kiln washed side down, on top of the glass.  Be sure the spacers are in places where they can support the upper shelf.

If you are thinning from 6mm to 3mm, normally you do not need any additional weight on top of the upper shelf.  But the thinner you want the glass to be, the greater the weight needs to be.  It could be another shelf, fire bricks or steel weights.

When scheduling the annealing remember you must take account of the mass of the weight on top of the glass.  You will need a much longer temperature equalisation soak and a much slower annealing cool.  

Further information is available in the ebook Low Temperature Kiln Forming.