Designing a Pattern Bar

Assuming that you are not going to just dump your scrap glass in a random pattern to form a pattern bar, you need to spend some time designing it.

The simplest kind of bar is composed of strips of glass which are stacked or assembled in the kiln, but there are many other more elaborate configurations.

Because of the additional annealing time required for larger and thicker items, most pattern bars range from 1" by 1" to no larger than 2" by 2". The length of the pattern bar can be any length, up to the maximum that will fit in your kiln.

The design process begins by thinking about the cross section of the bar. This is what will appear when cut and assembled. As a simple exercise, assume you are making a diamond pattern in the bar. You can draw this out using 3mm as the thickness (or 1.5mm if you are using thin glass). Rough out the pattern and then begin using 3mm as the grid. Remember that you will need to cut your strips 4mm or wider to obtain a clean break. As you plan it out you will see that you need one length at the base one half of the space remaining after you have laid down the first, central piece for the diamond. The next layer will have two strips for the diamond, giving a requirement for one strip to fill the space between the two for the diamond shape and two strips each one half the remaining space. This process goes on until the area is filled.

Pattern Bars

A pattern bar is a thick bundle of glass that has been fused together. These can be in the shape of a rectangle, or can be a thick pot melt – whether a disc or a rectangle. The length of the individual bars can be as long as your kiln allows, but needs to be practical to handle when cutting.


The basic steps involved in making a pattern bar include deciding on a design –whether controlled or random, cutting glass for the bar, assembling the cut glass into the desired bar shape, then firing to a full fuse. Once fired, pattern bars can be cut into slices with a saw - tile, glass, lapidary, or stone – which uses water for cooling and lubrication. The individual slices are then assembled and re-fused to make bowls, platters, and similar shapes. They can also be used as accents in any number of applications.

There is a caution about using pattern bar pieces. As the glass in the bars has been fired to a relatively high temperature, some of the characteristics may have changed. So you need to do a compatibility test before doing the main piece.

Designing Pattern Bars
Boxes for Pattern Bars
Dams for Pattern Bars