Wednesday 5 November 2014

Recognising Devitrification


The appearance of devitrification varies from mild streaks as a dirty appearance on the surface, to at worst a granular surface that breaks away in small pieces. The glass will often have raised sharp corners in cases of severe devitrification.



Avoiding devitrification relates to cleaningfiring rapidly through the devitrification rangeavoiding devitrification-prone glasses, and grinding edges as little as possible.



Repairing devitrification requires the removal of the devitrified surface. This can be done by sandblasting, sanding the surface by hand, using acid pastes to remove the surface. Then the piece needs to be fired again to a fire polish.



To ensure a polished surface a devitrification solution may need to be applied. It can be a commercial product or a borax solution.  Any devitrification solution should be applied evenly.

Wednesday 29 October 2014

Spray nozzles


Quite a bit of the material we spray is solids in a colloidal suspension. This means that the nozzle can clog easily. Frequent agitation is needed to keep the material in suspension and not building up on the bottom which can clog the screen at the bottom of the tube.




You should not have long delays between spraying in one session, as the solids can begin to solidify within the spray head and so clog it.

When you have finished spraying, take the spray head off and clean it completely and thoroughly to ensure there are no solids left to harden. Then put it back together and it should be clear for the next use as well as sealing the container.




Wednesday 22 October 2014

Stainless Steel Preparation


Preparing stainless steel rods and moulds for kiln work is done slightly differently from ceramic moulds.

Just to ensure that the steel is of the right grade, I fire it in the kiln to about 720C. This ensures that if the steel is not adequate for the high temperature work, you will find out that it spalls before the glass is put on top. It also has the advantage of removing any dirt and oils on the surface of the metal.




The separator that you need to put on the steel can be done cold if you use MR97 or other boron nitride coating. Its main advantage is that it can be put on cold and also that it has a very smooth surface. This should be put on thinly, or it will come off onto the glass.



You can also put standard kiln wash on the metal. The metal needs to be dry and clean. It could be sandblasted if desired for a bit of extra “tooth”, but is not normally necessary. Heat the metal to about 120C – 150C in the kiln. Remove it from the kiln with tongs or similar thing to grasp the hot metal. Spray or paint the kiln wash solution onto the hot metal. Return it to the kiln as necessary until you have a coating all over the metal. It does not have to be even all over, but noes need to have all of the metal covered.



If the kiln wash boils off the metal, it is too hot. So turn the kiln down a bit.
If the kiln wash runs off without sticking at all, the metal is not hot enough and needs to be returned to the kiln to heat up.
It is best to avoid applying the kiln wash to the metal in the kiln, as water and the hot elements do not mix well.

Wednesday 15 October 2014

Making Tests


Every time you get a kiln that is new to you – whether new or second hand – you need to do some tests. Recording these tests is essential to your future work.

The first test is to get to know your kiln – where are the hot and cool spots, what effect does the kiln produce at a given temperature and soak. A very good guide to knowing the temperature differentials in your kiln is given by Bullseye Tech Note 1 – Knowing Your Kiln 

The second test is to make a series of small scale tiles to know what your kiln does at different temperatures and rates of advance. What combination of rate and temperature gives the roundness, degree of tack, flat fuse that you want.
How does the kiln perform in slumping and what are the effects of thickness and number of layers on the rate of slump.

These are elements that you may feel are a delay in being able to experience the enjoyment of fusing. However, they are essential to the long term enjoyment and success of your fusing activities.


Wednesday 8 October 2014

Writing a Schedule


Making your own Schedule

I've been asked about making a schedule rather than using a pre-programmed one. My response is this, but please join in with amplifications and questions.

In principle, a firing schedule for glass follows these stages:
1 – a gradual, steady heat up to a temperature above the annealing point to avoid thermal shock
2 – a soak or slow rise around the slump temperature to allow any air to escape
3 – a more rapid rise to top temperature to avoid devitrification
4 – a rapid fall in temperature to an annealing soak, saving time and avoiding devitrification. The soak at annealing temperature is to equalise the temperature throughout the glass
5 – a steady slow fall in temperature to well below the lower strain point to complete the annealing
6 – a controlled cool to near room temperature to avoid thermal shock.


The details of schedules can appear complex, but the purposes of these six stages are reasonably simple.
Segment 1 is to heat the glass evenly without causing it to break from too fast an increase in temperature. At minimum this steady increase in temperature must continue to about 40ºC above the annealing point. (This will be about 540ºC)
Segment 2. This segment can include a “bubble squeeze” to enable air to get from between sheets of glass before the edges seal, or it can be a separate segment in your schedule. The slow rise in temperature will occur from about 600ºC to 680ºC. The bubble squeeze soak occurs at around 660ºC to 680ºC. In both cases there is normally a soak of half an hour at least at the end of the range.
Segment 3 is to go through the devitrification range (say 700ºC to 760ºC) as quickly as reasonable, but usually no faster than 330C per hour.
Segment 4 is to get back through the devitrification range to the annealing soak, which will be as long as required to equalise the temperature within the glass. This soak time increases exponentially with the thickness.
Segment 5 is the annealing cool, which should be a slow steady fall in temperature to ensure the glass all cools at the same rate (to around 370C).
Segment 6 continues the cool, although faster than previously, and often is achieved by turning the kiln off and leaving it closed until room temperature.

A schedule for a 6mm piece up to 2/3 the size of your kiln could be even simpler:
Segment 1 - 220 dph to 670C for 30 minutes
Segment 2 - 330 dph to 800 (flat fuse) for 10 minutes
Segment 3 - afap to 516 for 30 minutes
Segment 4 - 80 dph to 370, no soak
Segment 5 - off

You may find a schedule that will work, but you still need to know why it works, or at least what each segment is doing. So, for example, you need to think about what a 15 minute soak at 225C will do. What is the glass doing at that temperature? What do you want to achieve in that temperature range? Is there another way to achieve your objective? These are the kinds of questions you need to think about so you can construct your independent schedule when you move outside the parameters of the pre-programmed schedules.

To make a schedule for yourself can be worrying. But you can see from this example that it does not need to be complex. The principles are simple, although the details can be confusing. It is essential to know something about how heat affects the glass and this Bullseye Tech Note is one of the best descriptions. 
Knowing what the heat up events are is useful too. 

Wednesday 1 October 2014

Selecting a Kiln


Kiln Forming – Selecting a Kiln
You have been doing some fusing and slumping and now want to get into kiln forming in a serious way. So you need to get a kiln.

The basic kiln choices are ceramic vs. glass. The brand, model and size are up to you. But there is some helpful information on the advantages of each kind of kiln in this post.

Another consideration is the shape of the kiln. Generally the greater the area of the shelf in relation to its size, the better it will suit fusing and kiln forming. Oval kilns seem to waste some space, although they do not have cool corners like the rectangular ones do. Relatively deep and round kilns are best for casting and high temperature work.

Even before you buy the kiln you need to think about where you will be installing the kiln and that will have an effect on the model and size. Some considerations are here.

Think about the kind of work you want to do. This will change with time, but you cannot anticipate that now. Will you be doing jewellery scale, detailed work, lots of forming work, high temperature or even casting work. Each of these have different requirements.

Small kilns are best for jewellery and detailed work – they can be fired quickly and will reach the top and annealing temperatures with a minimum of delay.

If you tend to work larger then you should consider a kiln of about 40 cm square to start with, although smaller kilns will work if they have enough height.

Slumping and kiln forming put a premium on height. If you are going to be doing a lot kiln forming you should consider a kiln with at least 25cm from base to elements. Ex-ceramics kilns can be good for this.

If you are going to be doing a lot of high temperature work, such as casting, pot melts, pattern bars, etc. you might want to consider a brick lined kiln such as a ceramics one as they retain heat by design longer than those designed for glass.

There are a lot of models, so it is up to you to find the combination of style, shape, size and price that suit your present needs.

Wednesday 24 September 2014

Selection of a Training Course

Often selecting training in glass is a lottery. It most commonly is done through propinquity and incidental knowledge. Most often a course is chosen because information came to hand of a class that is being held nearby. These are not always the best criteria. It may be better to travel for a course that fits your needs better.

There are some things that you can check to help determine whether the course being offered is the one for you.

The first of course, is whether the instruction will meet your interests. Yes, the title has caught your attention, but you need to find out if the syllabus covers your area of interest adequately. 
· Inquire for a syllabus or teaching outline. If there is not one, you may have a question on whether the course is well planned, as well as whether it deals with your interests.
· Ensure the course level is appropriate to your needs. Are there any prerequisites in terms of experience or ability?

Another important element in selection is the person who is leading the course. The leader may of course, may have brought in teacher for this subject, so you need to know things about both. 
What is the background to the course leader? Some of the things you might want to find out are:
· Is the course leader part of a business providing materials,
· Is it in a centre of excellence
· Is it an accredited education provider
· Is the leader a studio owner or artist
· What is the history or experience in providing training courses
Who is the teacher? Some to the things you should ask about in addition to the person’s identity are:
· What is known about her/him? Is there a CV available?
· Where examples of work can be seen
· What experience does the person have in making in general and in making using the technique(s) being offered?
· What length of teaching experience does the person have?

Having satisfied yourself about the instructor(s) you need to begin doing some comparisons with other course offerings. Price is always important, but you need to know what value you are getting, so you need to know what is included in the price. Some of the things that affect price and value are:
· Tools – are they all included, or do you have to provide your own?
· Materials – are the materials included in the price or do you buy as you use?
· Equipment – is the use of all the machinery and facilities included? What is excluded?
· Food – are meals included and which ones? What refreshments are available?
· Length of instruction time – how many days are involved? What are the hours of instruction? Are there any extensions of instruction or working time?
· Numbers – what is the expected teacher to student ratio? This will affect the amount of time you receive from the teacher.
· Accommodation – if relevant, is it included? Is there any assistance in obtaining accommodation?

You should also find out about booking, deposits, cancellation conditions, and when payment is due.

Another element relevant to selection is the premises in which the course is to be held.
· Are they purpose built for the relevant activities?
· Are the premises general educational accommodation? Is it local authority classroom provision? Etc.
· Is the instructor’s studio being used? What space is available?

An obvious important element in selection is convenience.
· Location – is it near or easy to get to?
· Time - are the days convenient? Is the time of the day appropriate?
· Duration – how long are the sessions?

A really important element in selection is the evaluations by past students. These are difficult to get, and if supplied by the instructor, are open to doubt. The best source of evaluation is direct contact with past students. It is important to ask friends and other people in the field about the course being offered.

Documentation about the course is helpful in getting a feel about what is being offered. This might include information about the instructor(s), description of course, dates, times, cost, information on level of instruction, location, travel, facilities, and accommodation.

It is unlikely that you will get the best fit in every category. You will need to make compromises on various elements, so it is important that you think about what you want from the course. If there are one or two elements that you feel are important but not covered, you should contact the provider and ask about whether any accommodation to these requirements are possible.

Wednesday 17 September 2014

Screens for Melts




You can buy various stainless steel screens such as barbecue grids for supporting glass melts. The grids need to be of stainless steel. Type 304 is the most common, but there are other grades which work at high temperatures too [link to stainless steels]

You can make your own grid as Cynthia Morgan does. This provides a more flexible arrangement for various effects. 

Instead of imbedding the rods into the brick, you could also place them on top. Place a kiln brick or other kiln furniture on the ends of the rods to secure the metal from moving. Then you can put the glass on top of the rods without them shifting as the glass is placed.



Wednesday 10 September 2014

Stainless Steel for Kiln Uses


The reason for using stainless steel is that it differs from carbon steel by the amount of chromium present and reduces the spalling. Unprotected carbon steel rusts readily when exposed to air and moisture. This iron oxide film (the rust) is active and accelerates corrosion by forming more iron oxide, and due to the greater volume of the iron oxide this tends to flake and fall away (spall).


Stainless steels contain sufficient chromium to form a passive film of chromium oxide, which prevents further surface corrosion by blocking oxygen diffusion to the steel surface and blocks corrosion from spreading into the metal's internal structure, and due to the similar size of the steel and oxide ions they bond very strongly and remain attached to the surface.


There are a number of grades of stainless steel. Some of the ones that perform better in hot conditions are:

300 Series—austenitic chromium-nickel alloys. Austenitic steels have a cubic crystal structure. Austenite steels make up over 70% of total stainless steel production. They contain a maximum of 0.15% carbon, a minimum of 16% chromium and sufficient nickel and/or manganese to retain an austenitic structure at all temperatures from the extremely cold to the melting point of the alloy.

Type 304—the most common grade; the classic 18/8 (18% chromium, 8% nickel) stainless steel. Outside of the US it is commonly known as "A2 stainless steel", in accordance with ISO 3506 (not to be confused with A2 tool steel).

Type 304L—same as the 304 grade but lower carbon content to increase weldability. Is slightly weaker than 304.

Type 304LN—same as 304L, but also nitrogen is added to obtain a much higher yield and tensile strength than 304L.

Type 309—better temperature resistance than 304, also sometimes used as filler metal when welding dissimilar steels, along with inconel.

Type 316—the second most common grade (after 304); for food and surgical uses; alloy addition of molybdenum prevents specific forms of corrosion. It is also known as marine grade stainless steel due to its increased resistance to chloride corrosion compared to type 304.

Type 316L—is an extra low carbon grade of 316, generally used in stainless steel watches and marine applications, as well exclusively in the fabrication of reactor pressure vessels for boiling water reactors, due to its high resistance to corrosion. Also referred to as "A4" in accordance with ISO 3506.

Type 316Ti—variant of type 316 that includes titanium for heat resistance. It is used in flexible chimney liners.

Type 321—similar to 304 but lower risk of weld decay due to addition of titanium.

400 Series—ferritic and martensitic chromium alloys

Type 439—ferritic grade, used for catalytic converter exhaust sections. Increased chromium for improved high temperature corrosion/oxidation resistance.

Type 446—For elevated temperature service


500 Series—heat-resisting chromium alloys


Based on Wikipedia 

Wednesday 3 September 2014

First Firing


Even if this is not your first kiln there are a number of things to do when starting.

The first is to read the manual. Obvious, but in our enthusiasm to get started, reading seems boring. It is essential to understand what the manufacturer wants you to do and to understand how the kiln and controller work.

Then, you can prepare kiln. Test fire the kiln empty to make sure it works and burn out any binders remaining in the kiln materials. You can do this firing at about 400C/hour as there is no glass to damage. Fire to around 800C. Then you can shut off, or programme a dummy anneal. This also ensures you know how to work the controller.

While waiting for the kiln to complete the fast test firing, read the manual again.

When the kiln is cool, apply kiln wash to the bottom (if it is brick) and lower sides, below any side elements. If the bottom or sides are fibre, no kiln wash is required. Kiln wash the shelf and any kiln furniture too.

Now is the time to test for how even the heat is in your kiln. Arrange the kiln furniture around the shelf as described and put glass over. The kiln furniture can be any refactory material, even folded 3 mm fibre paper will be strong enough to hold the small pieces of glass above the shelf. Fire the kiln as described in the Tech Note 1.

Now try out the suggestions in the manual, especially the programming of the controller, even if it has pre-programmed schedules. Look at Bullseye and Spectrum sites to get sample schedules. Enter these as trial schedules.

Then you should be ready to fire the first piece of glass. Place the glass in the kiln, programme it, and record the information about the firing. Now turn the kiln on for the first real fuse.

Wednesday 27 August 2014

Cleaning Glass Before Painting



If your glass is not really clean, you can get gaps in the paint line. You may also have areas where the paint beads up rather than flows evenly.

You need to clean as best as possible first. Then just before painting you can use a dilute solution of the paint to scrub all over the glass with your finger or other firm material. Wipe any residue off with a paper towel and you will find that the prepared paint will flow evenly onto the glass.


Wednesday 20 August 2014

Fiber Paper Safety


There are often concerns raised about safety relating to the dust from Thinfire, a trade marked product from Bullseye. These concerns also apply to the Spectrum product called Papyros. The main constituents of these are cellulose, aluminium hydroxide, fibre glass and organic binders. It therefore is mainly a nuisance dust and irritant. Greg Rawles, a certified industrial hygenist with a scientific and common sense approach, says that the toxicology of fibre glass is not yet determined. So the best idea is to wear a P95 respirator while dealing with the dust – mainly the cleaning phase of dealing with the shelf. He also recommends keeping the kiln closed during the burn-out phase of the binders, although others recommend venting to avoid anything settling on the glass during the burn-out.

Some people seem to have skin reactions to dust including that from Thinfire and Papyros and tend to wear gloves. If you are wearing rubber or latex gloves for extended periods, it may actually promote a reaction to the gloves rather than a primary reaction to the dusts of the paper. So checking on alergic reactions to the gloves is advisable in addition to the dust. 

If in fact, you are reacting to fibre paper dust, consider using kiln wash instead. If this is not practical or desirable there are several things you should do.
  • Use gloves (for those with sensitive skin),
  • wear long sleeved high necked shirts and pull the gloves over the ends of the sleeves to prevent dust getting to your skin,
  • vacuum the kiln with HEPA filters,
  • dampen the powder with water spray before brushing,
  • take precautions against taking the dust home by changing in the studio and placing clothing in plastic bags to take to the wash.


Wednesday 13 August 2014

Black Specks in Mesh Melts


The first time you use a mesh for a melt, it doesn't spall until it cools. By that time, the glass has hardened enough that any black specks of metallic oxidisation just land on the top of the melt and can be brushed away.

But, once a mesh has been fired previously, it can spall and drop little bits at any time during the firing process, so some of the bits get embedded in the glass.

The only way I have found to prevent this is to sandblast the mesh between firings to remove any loose flakes of metal. This is time consuming enough that you may wish to use a new piece of mesh for each melt. The alternative is to ensure you are using stainless steel as the grid.

There are several options for grids.

Wednesday 6 August 2014

Applying Kiln Wash


Kiln wash, or batt wash as used in the ceramics field, is largely made up of alumina hydrate, kaolin (china clay), and often some colouring to indicate an unfired shelf.

These solids are heavy and settle to the bottom of the container quickly. So, you have to agitate the contents with each dip of the brush onto the liquid. To provide adequate - and even – coverage of the shelf, mould or other refractory material, you should paint in four directions. Up, down and the diagonals. You need to apply just enough that you do not see the shelf surface.

Alternatively you can spray the solution onto the surface. This is an easier way to get an even covering, but it sometimes is overly stippled.

A tip I was given for the smoothest kiln shelf is to level the damp prepared shelf and spray a layer of warm water over the wash to form a very shallow puddle. As the water is absorbed into the shelf, the only limitation to the smoothness of the surface is the granular nature of the kiln wash.

Saturday 2 August 2014

Layering Glass Textures


When using textured glass there is a decision to be made on whether the smooth or textured side is up.

Oddly, the largest, but thin bubbles occur when putting the smooth sides together. it seems that as the glass is not perfectly flat, it holds air within the fused piece.

The fewest bubbles seem to be promoted by placing the rough side down on all pieces. This is easy as cutting is done on the smooth side anyway, and so no reverse cutting is required. It seems that the rough side of the glass provides ways for the air to escape during the bubble squeeze although it does promote micro bubbles within the glass.

If more bubbles are desired, you can place the textured sides together. That seems to allow the majority of the air out, but still leaves the micro bubbles from both sheets.

I have had good results following the Bullseye recommendation to keep the smooth side up on all layers. 

Wednesday 23 July 2014

Re-firing Poorly Annealed Items

Sometimes you suspect a piece has not been adequately annealed and want to re-fire it to make it sound. The question arises as to how quickly it can be re-rfired.

These pieces are very easy to heat shock, so the initial rate of advance needs to be much slower than for any piece of the same size, possibly less than half the usual rate. This slow rate should be steady without pauses until about 540ºC, which is above the annealing point of most fusing glasses. At this point you can speed up the rate of advance to whatever your normal one is.

Of course, it is best to anneal each piece on each firing to the extent that there is no question  that the piece is properly annealed. Looking at the Bullseye project notes and the annealing of thick slabs can help for evenly thick items. For tack fused and items of uneven thickness, you could review this posting.

Saturday 19 July 2014

Diagnosis of Breaks in Kiln Formed Glass

Often more can be learned from failures than a number of successes. A common failure in kiln forming is broken glass. The appearance of the break will tell you a lot about the problem so that you know where to look for the solution.

Cracks and breaks can occur at various times in the kiln. These will have occurred by the time you open the kiln:
  • Curved cracks and breaks are usually caused by inadequate annealing. Often the break will have a hook or sharp curve near the edge of the glass. The edges will be sharp.
  • Cracks and breaks occurring where two pieces of glass meet is usually an indication of incompatibility between the two glasses. This means that you need to perform a compatibility test with the two glasses. Sometimes it is caused by a large difference in the thickness of the glass, especially when light and dark glasses are side by side. This is normally an annealing problem.
  • Breaks in the piece (often more than one) with rounded edges indicate a thermal shock break caused by raising the temperature too quickly for the size or thickness of the piece.
  • Breaks that cross the piece in a reasonably straight line, going across and through pieces of glass are an indication of thermal shock.  The line will be rounded or the pieces even formed together again if it was shocked on the rise in temperature.  If the piece was cooled too quickly, the edges will be sharp.
  • Multiple breaks into small pieces - normally sharp - are an indication that the glass has stuck to the shelf or kiln furniture. This is caused by inadequate batt wash on the shelf and kiln furniture. It tends to happen with high temperature firings more than lower temperature firings.
Other cracks and breaks occur after the piece has cooled.
Breakage occurring long after a piece has been completed are an indication that the stress within the glass has overcome the strength of the piece. There are several possible individual and combined factors:
· improper annealing,
· thermal shock,
· incompatible glass,
· wear and tear.

But the most likely problem is inadequate annealing. Unless you have access to your firing records and can determine how the piece was fired and the materials used, you will need to accept it as experience and extend future annealing times.

The best cure for these is prevention.

First is to do a compatibility test to determine if the glasses fit together in the combination you plan for your piece.
Second, if you check the stresses of the flat piece between polarizing filters, you will be able to see if there are stresses within the piece before you do any further kiln forming with this glass or setup. If the stress is from incompatibility - where you see the stress halos around specific pieces of glass - you will need to destroy the piece. If the stress is more generalized, you can put the piece back in the kiln, reheat slowly and soak at the annealing point for a longer time and use a slower annealing cool.

Wednesday 16 July 2014

Organic Burnout Marks

Occasionally there is a haze at the centre of the back of large pieces of fired glass. This seems to happen when a large piece of glass is placed over fibre paper (of whatever thickness) that has not been pre-fired. 

 This is based on my experience of doing large pieces on thinfire or other fibre paper with a relatively fast rate of advance. What seems to happen is that the edges of the glass soften enough and early enough that not all the binder in the fibre papers can burn out and the combustion gasses escape from under the glass. The resulting haze is the remnants of the combustion product fired to the surface of the glass.

I have found that flipping the piece over and taking the glass to a low temperature fire polish is enough to return the glass to its usual appearance. You can, for extra insurance, apply a devitrification spray, although I have not found it necessary.

You could, of course, work the back of the glass with pumice and cerium oxide to bring back the original shine without firing. But my impression is that the areas with haze are fractionally depressed into the back surface. This means that a lot of glass has to be removed to reach and polish the hazy areas.




Wednesday 9 July 2014

Effects of Multiple Layers

Stacking layers of glass fully or partially over the base layer has significant effects on the firing of the whole piece.

Glass is a poor conductor of heat, so you need to be careful to allow the heat to penetrate to the base layer to avoid thermal shock. There also is the effect of the (very small) insulating space between each sheet. The effects of multiple, even layers can be seen from this table based on Graham Stone's* work:

3mm layers
1 sheet – Initial Rate of Advance =1000ºC to 475ºC (less than half an hour)
2 to 3 layers – IRA = 240ºC to 475ºC (ca. 2 hours)
4 layers – IRA = 100ºC to 475ºC (4.75 hours)
6 layers – IRA = 25ºC to 125ºC, then 30ºC to 250ºC, then 40ºC to 375, then 50ºC to 475 before 150C to top temperature (ca. 15.5 hours)

This shows the dramatic effect increasing the number of layers has on the firing schedule to make sure the heat gets to the bottom sheet evenly. If you compare the initial rates of advance (IRA) with the same thickness, but fewer sheets you can see the space between layers is important.

6mm layers
1 sheet – IRA = 320ºC to 475ºC (ca. 1.5 hrs)
2 layers – IRA = 240ºC to 475ºC (ca. 2 hrs compared to 4.75 hrs for 4 layers of 3mm)
3 layers – IRA = 200ºC to 475ºC (ca.2.5 hrs compared to 15.5 hrs for 6 layers of 3mm)

These are the fastest safe firing speeds for evenly covered sheets. 

This difference in firing times for stacks of thicker glass, shows how important it is to fire sections of the stack before the final firing of all the layers together.  It also reduces the risk of bubbles developing within the stack. 

If you are thinking of tack fusing with thicker and thinner areas, you need to take account of the differences in thickness in the various areas of the piece when preparing your schedule. You will need to decrease your IRA by quite a bit. So you might want to be thinking of firing some of your pieces to be added to the base layers before tacking them in an additional firing to reduce the risk of thermal shock to the base layer.


* Firing Schedules for Glass; the Kiln Companion, by Graham Stone, ISBN 0646 39733 8

Wednesday 2 July 2014

Cleaning


A lot of devitrification resembles dirty smears over the glass that will not clean away. This kind of devitrification results from inadequate cleaning.




The glass needs to be made “squeaky clean”. The glass needs to be free of dust, oils and minerals before firing. An initial wash of the glass with a minimum amount of liquid soap will dispose of the dust and oils. However it may leave behind minerals and additives from the soap and water, so a rinse in clean water followed by a polishing with unprinted paper towels or lint free cloths washed without softeners. As the glass dries you may very well hear the squeak of glass that is well polished to dry.



If there are still residues of labels or markers, use of a spirit may be required to remove these marks. Then the glass will have to be cleaned again in the normal way to remove the residues from the spirits.



If you are fortunate to be in an area with very few minerals in the water, you will not have to take as many precautions as those in areas with hard water. If you have hard water, you may need to think about using distilled water for the final rinse if you have streaks of devitrification after the standard cleaning process. The use of spirits is not necessary. The glass still needs to be polished dry with unprinted paper or dedicated towels.

An alternative (that I use most often) is to use a window cleaner without additives, such as supplied by glaziers. This avoids the local water supply, and most often is sufficient to remove dust and oils.

Wednesday 18 June 2014

Slowing the Rate of Advance


The question is sometimes asked whether the rate of advance in a firing schedule should be slowed when re-firing; for a fire polish for example.

Cynthia Morgan contributes four circumstances where you would want to slow the rate of advance:
1) On the previous firing you were fusing a whole bunch of little pieces into a much thicker piece, so you need to reduce your ramp to avoid thermal shocking the thicker glass
2) You think you might not have annealed the piece well enough on the previous firing, so you're playing it safe
3) You suspect there's a crack somewhere in the piece (from cold working or whatever) so you're reducing the chance it will expand quickly and open the crack
4) You've got to do something to the glass/kiln at a certain point in the firing cycle, and if you go at your normal rate you'll wind up doing it at 3AM...so you slow down the firing and get more sleep.

Otherwise, well-annealed is well-annealed. If none of those four conditions obtain, I don't see why you'd need to slow down”.


Wednesday 11 June 2014

Cleaning Frit and Powder


If you make your own fine frit and powder, make sure it is clean to avoid black specks, or a grey appearance caused by metal dust and fragments.

Clean the glass you are going to break up before you start the process.
Use mild steel or other magnetic metal to break up the glass, or protect the glass from the breaking tools with layers of paper, plastic, cloth or combinations of these materials.

Then with a powerful magnet remove any metal residue from the frit and powder. The magnet will need to be passed over and through the glass particles a number of times, cleaning the magnet after each pass. To ease the cleaning you may wish to put the magnet in a plastic bag. Then move the bag over the waste bin and remove the magnet. The particles fall into the bin.

Do not use stainless steel to break up the glass as it will not be attracted to the magnet. Stainless steel particles will result in the same discolouration as if you left the glass uncleaned.

Wednesday 4 June 2014

Super Glue Safety


Super glue is frequently used as a temporary fixative in assembly of kiln forming projects. There is some concern about safety, as it is known that super glue is made from cyanoacrylate, which it is feared will break down in the kiln into cyanide gas.

Greg Rawls, a certified industrial hygienist says "I looked at the MSDSs for several forms of super glue. The main component is Ethyl 2-cyanoacrylate, which has a TLV of 0.2 ppm which is relatively toxic. [However,] the thermal decomposition products are carbon monoxide and carbon dioxide. I did not see a reference to cyanide gas. However, as I recall cyanide gas dissociates into elemental carbon and nitrogen at about 800 F. Since you use it in such small quantities, I would not worry about it. In my opinion the worst thing that could happen is you glue your fingers to the glass."

Safety issues

To treat the safety issues seriously and determine if you feel Greg Rawls' view is justified, you need to look at the issues of toxicity, reactions, adhesion of tissue, ventilation, first aid and decomposition products in the whole context.

Toxicity
The fumes from cyanoacrylate are a vaporized form of the cyanoacrylate monomer that irritate sensitive membranes in the eyes, nose, and throat. They are immediately polymerized by the moisture in the membranes and become inert. These risks can be minimized by using cyanoacrylate in well ventilated areas. About 5% of the population can become sensitized to cyanoacrylate fumes after repeated exposure, resulting in flu-like symptoms. It may also act as a skin irritant and may cause an allergic skin reaction. On rare occasions, inhalation may trigger asthma. There is no single measurement of toxicity for all cyanoacrylate adhesives as there is a wide variety of adhesives that contain various cyanoacrylate formulations.

The United States National Toxicology Program and the United Kingdom Health and Safety Executive have concluded that the use of ethyl cyanoacrylate is safe and that additional study is unnecessary. 2-octyl cyanoacrylate degrades much more slowly due to its longer organic backbone that slows the degradation of the adhesive enough to remain below the threshold of tissue toxicity, so the use of 2-octyl cyanoacrylate for sutures is preferred.

Reaction with cotton

Applying cyanoacrylate to some materials made of cotton or wool results in a powerful, rapid exothermic reaction. The heat released may cause serious burns, ignite the cotton product, or release irritating white smoke. Users should not to wear cotton or wool clothing, especially cotton gloves, when applying or handling cyanoacrylates.

Adhesion of the Skin

Various solvents and de-bonders can be used. These include:
Acetone commonly found in nail polish remover, is a widely available solvent capable of softening cured cyanoacrylate
Nitromethane
Dimethyl sulfoxide
Methylene chloride
Commercial de-bonders are also available.

Warnings include:
  • It is a mild irritant to the skin.
  • It is an eye irritant.
  • It bonds skin in seconds.
  • Any skin or eye contact should be copiously flushed with water and medical attention be sought immediately.
  • Do not attempt to separate eye tissues – the bond will separate naturally within a few days.

Precautions
  • Use goggles.
  • Do not wear cotton or wool clothing while using super glue
  • Ventilate the area well. Since cyanoacrylate vapours are heavier than air, place exhaust intake below work area. Activated charcoal filters using an acidic charcoal have been found effective in removing vapours from effluent air so the bench top air filters are suitable for use while using super glue.
  • Avoid use of excess adhesive. Excess adhesive outside of bond area will increase level of vapours.
  • Assemble parts as quickly as possible. Long open times will increase level of vapours.


Evaporation Effects
  • The effects of heating cyanoacrylate are not completely known. The flash point is known to be greater than 85ºC. As a precaution do not remain in the area of the kiln after that temperature has been reached.
  • The decomposition products are carbon monoxide and carbon dioxide. There is no reference in the literature to cyanide gas. It is highly unlikely that heat will cause the release of cyanide gas at any time during the heating. To be certain, you should make sure the evaporation of the glue is be complete before firing the kiln.

See this tip for the use of super glue in kiln forming.

Wednesday 21 May 2014

Pre-Set Schedules


Moving on from pre-set schedules

If your kiln has come with pre-set schedules, the first thing to find out is what rates, temperatures and times are set for the fast medium and slow fuse, tack and slump schedules.

Then, rather than just pressing the appropriate button, enter the numbers into the controller for each firing. This will give you confidence in programming the firings. Alter one element (such as the rate of advance, or the soak length) each time you enter the schedule and record the results. This will enable you to see what different rates, temperatures and soaks will do to your glass.

Make quick observations for fusing from about 750C every quarter of an hour to see how the glass is reacting. For slumping the observations should start about 600F. If the glass has reached the state you want before that segment of the schedule has completed, just advance the programme to the next segment (read your manual to find out how to do that on your controller).

It is only by making alterations and observing the results that you will gain the confidence to do your own programming when you do something the manufacturer didn't think about. There are so many factors, the programmes work for a limited range of possibilities.