Elevation of Moulds

Is it necessary to elevate slumping moulds above the shelf? 

I first heard of the need to elevate moulds from a Bhole representative about 2007. I ignored it, but didn't get around to testing until working on my e-book Low Temperature Kilnforming.

That work showed there is a larger difference in air temperature above and below the unsupported mould than the supported one. But that difference is much smaller than between the air temperature and the glass.

At 150°C/270°F per hour the maximum difference in the temperature under the mould between the elevated and on-the-shelf mould at top temperature was 41°C/74°F while the air temperature difference was 126°C/227°F higher than under the elevated mould.  Many of the tests showed less difference than the maximums given here.

By reducing the ramp rate from 150°C/270°F per hour to 120°C/216°F, the under mould to above mould differential was reduced by a quarter. I didn't test beyond that. But it would appear that slower rates of 100°C/180°F and less will reduce that differential.

The graph also shows that there is a large difference between what the pyrometer reads than the mould temperature of the slump. Slower ramp rates produce an air temperature much closer to the mould temperatures.

Shortly into the rapid cool towards anneal soak and cool only minor temperature difference showed between elevated and on-the-shelf moulds throughout the anneal soak and anneal cool.

These details make it clear to me that elevating moulds is completely unnecessary with slow ramp rates. This of course, fits with the low and slow mantra that many of us promote. However elevating the mould will not harm the slump.

One caution, though. Damp. Wet, or heavy moulds must be supported to avoid breaking the shelf. So I advocate placing these moulds on the floor of the kiln with 2cm posts, rather than on the shelf. I don't know if it is necessary. I haven't tested it. But I do know that moulds in this condition will break the shelf without significant separation between the two.